1 SCOPE
Thisstandardspecifiesthemethodsfordeterminingthehexavalentchromium(Cr(VI))contentinautomobilepartsandmaterials,where,
X-rayfluorescencespectrometryisapplicabletoscreeningandrapiddeterminationofCr(VI)contentinautomobilematerialsbyusingX-rayfluorescencespectrometry.
Qualitativetestforthepresenceofhexavalentchromiuminanti-corrosivemetalcoatingsisapplicabletodeterminingthepresenceofCr(VI)inanti-corrosivecoatingsofautomobilesbyusingspot-testprocedureandboilingwaterextractionprocedure.Determinationofhexavalentchromiumcontentinanti-corrosivemetalcoatingsisapplicabletodeterminingtheCr(VI)contentinanti-corrosivecoatingsbyusingboilingwaterextractionprocedureandcolorimetricmethod.Theabovetwotestmethodsareapplicabletothecoatingswithoutanyadditionalcoveringlayer,e.g.oilfilm,water-basedorsolvent-basedpolymerfilmorwaxyfilm.
DeterminationofhexavalentchromiumcontentinpolymermaterialsandelectronicmaterialsisapplicabletodeterminingtheCr(VI)contentinpolymersandelectronicsbyusingalkalineextractionmethodandcolorimetricmethod,butnotapplicabletoPEorEVACmaterial.TheCr(VI)contentinotherautomobilematerials,e.g.glass,ceramics,fabrics,andpaintcoatings,canbedeterminedbyreferencetothismethod.
DeterminationofhexavalentchromiumcontentinleathermaterialsisapplicabletodeterminingtheCr(VI)contentinleathermaterialsbyusingphosphatesolutionextractionmethodandcolorimetricmethod.
2 NORMATIVEREFERENCES
Thefollowingreferenceddocumentsareindispensablefortheapplicationofthisdocument.Fordatedreferences,onlytheeditioncitedapplies.Forundatedreferences,thelatesteditionofthereferenceddocument(includinganyamendments)applies.
GB/T Steelproductzinccoatingmasstestingmethod(GB/T-,ISO:,MOD)
GB/T Rulesofroundingofffornumericalvaluesexpressionandjudgmentoflimitingvalues
GB/T MetallicandOtherNon-organicCoatings—DeterminationofMassperUnitArea—ReviewofGravimetricandChemicalAnalysisMethods(GB/T-,ISO:,IDT)
GB/T- RequirementsforProhibitedSubstancesonAutomobiles
GB/Z- Rapidscreeningoflead,mercury,chromium,cadmiumandbromineofregulatedsubstancesinelectricalandelectronicequipment-X-rayfluorescencespectrometry
QB/T- TermsforLeatherIndustry
QB/T Leather—Chemical,PhysicalandMechanicalandFastnessTests—SamplingLocation(QB/T-,ISO:,MOD)
IEC:Ed.1.0Electrotechnicalproducts—Determinationoflevelsofsixregulatedsubstances(lead,mercury,cadmium,hexavalentchromium,polybrominatedbiphenyls,polybrominateddiphenylethers)
ISO: ChromateConversionCoatingsonZinc,Cadmium,Aluminium—ZincAlloysandZinc-AluminiumAlloys—TestMethods
ENISO: Leather—ChemicalTests—DeterminationofChromium(VI)Content
3X射线荧光光谱法
3.1原理
将制备好的样品置于X射线荧光光谱仪样品室内,按所选定的分析模式对样品中的铭含量进行X射线荧光光谱分析,并根据筛选限值判断样品中铬含量是否合格,以及是否需要进行精确测定。
注:x射线荧光光谱分析所得结果是样品所含的总路而非六价铬。
3.2试剂和材料
3.2.1棚酸:优级纯℃烘1h储存于干燥器内。
3.2.2无水囚棚酸鲤:优级纯,℃灼烧轴,储存于干燥器内。
3.2.3液氮:工业级。
3.2.4含铭元素的标准物质。
3.3仪器和设备
3.3.1X射线荧光光谱仪。
3.3.2切割机。
3.3.3液氮低温粉碎机。
3.3.4研磨机:带碳化鸽(WC)磨具。
3.3.5压片机:工作压力不小于20MPa0
3.3.6熔样机:工作温度不低于℃。
3.4样品制备
3.4.1样品制备原则。
3.4.1.1用于分析的样品必须覆盖光谱仪的测量窗口。
3.4.1.2样品的照射面应能代表样品整体。
3.4.1.3样品制备过程中应注意防止污染。
3.4.2样品制备方法。
3.4.2.1固体样品。表面平整、大小适合X射线荧光光谱仪要求的均质样品,直接分析。小样品可汇在一起进行分析。薄样品,可将其叠在一起达到足够厚(厚度至少5mm),需特别注意样品厚度的一致性及组成的均匀性。分析时为使样品平整铺开,可加内衬材料作为支撑物,应尽量选用背景低的内衬材料。
各种块、板等不定形的样品以及尺寸过大的样品,可用切害IJ机、研磨机等将其加工至合适尺寸。
小样品(如塑料颗粒等)通过液氮冷冻、机械粉碎再经压片机压片制成分析样品。
玻璃、陶瓷等易碎样品先粉碎成小块,再研磨成小于目(0.mm)的粉末,混匀,用棚酸(3.2.1)衬底压片制样,厚度不小于1mm,或用无水四棚酸鲤(3.2.2)制成玻璃融片分析样品。
由不均匀材料组成的、无需或难以进-步机械拆分的非均质样品,将样品切割破碎,经液氮冷冻,用研磨机将破碎后的样品研磨成粒径不超过1mm的粉末状样品,混匀,用棚酸(3.2.1)衬底压片制样,厚度不小于1mm,或用无水囚棚酸鲤(3.2.2)制成玻璃融片分析样品。
3.4.2.2液体样品。移取一定体积的液体样品加入到液体专用样品杯里(样品厚度至少15mm),杯底部用6mm厚的聚脂膜支撑,杯上用带孔的盖盖住。